Título Magnetron sputter deposition of WC-Ag and TiC-Ag coatings and their frictional properties in vacuum environments
Autores ENDRINO ARMENTEROS, JOSÉ LUIS, Nainaparampil J.J. , Krzanowski J.E.
Publicación externa Si
Medio SCRIPTA MATERIALIA
Alcance Article
Naturaleza Científica
Cuartil JCR 1
Cuartil SJR 1
Impacto JCR 1.16800
Impacto SJR 1.47800
Web https://www.scopus.com/inward/record.uri?eid=2-s2.0-0036836453&doi=10.1016%2fS1359-6462%2802%2900236-1&partnerID=40&md5=78df4baf26c4560396872a5742b7cedf
Fecha de publicacion 01/01/2002
ISI 179142100008
Scopus Id 2-s2.0-0036836453
DOI 10.1016/S1359-6462(02)00236-1
Abstract Thin films of WC-Ag and TiC-Ag were deposited by magnetron sputtering for the purpose of analyzing their tribological properties in vacuum. X-ray diffraction was used to determine structural properties, and energy dispersive X-ray analysis was used to determine the relative atomic content of silver in the films. Pin on disk friction tests were performed to obtain the coefficient of friction in vacuum. The deposited films showed a structure containing separate carbide/silver phases, as was desired for providing both high wear resistance and low friction. The tribological test results show a significant decrease in the friction coefficient for both TiC-Ag and WC-Ag, to a minimum value of 0.2, with increasing silver content. © 2002 Acta Materialia Inc. Published by Elsevier Science Ltd. All rights reserved.
Palabras clave Coatings; Friction; Interfaces (materials); Magnetron sputtering; Scanning electron microscopy; Silver; Sputter deposition; Thin films; Tribology; Vacuum; Wear resistance; X ray diffraction analysis;