Olivares, D. , FERRADA MARTINEZ, PABLO DANIEL, Marzo, A. , Pinto, K. , Espinoza, D. , Rabanal-Arabach, J. , Portillo, C. , Fuentealba, E. , Llanos, J.
No
Sol. Energy
Article
Científica
6.7
1.373
01/01/2022
000741720800007
Soiling affects the economic profitability of solar photovoltaic plants, reducing productivity of the photovoltaic modules and increasing maintenance costs. Typically, studies on the soiling impact on photovoltaic technologies conducted outdoors require long exposure times. This paper deals with a new methodology for accelerated indoor test. Dust samples from the Atacama Desert are used to study physicochemical aspects of local soiling and its effects in the performance of solar cells. The new methodology is based on spin-coating to deposit homogeneous soiling layers on photovoltaic glass. This technique allows different soil mixtures to be deposited, resulting in the desired surface dust densities. X-ray diffraction and scanning electron microscopy of samples with artificially indoor and naturally outdoor deposited dust revealed similar behavior. In both, gypsum was the soluble material supporting the cementation process. The external quantum efficiency of the solar cell under different soiling conditions allowed to evaluate its effect on the photogenerated current density (J(ph)) for different spectral ranges. As expected from other studies, the influence of soiling is higher in the ultraviolet spectral range than at other wavelengths. It is observed that as the amount of deposited soil increases, the Jph losses are higher in the ultraviolet spectral range than in the visible or infrared. Because of the reduction in current density, efficiency is affected as the surface dust density increases. For instance, the efficiency decreased by 66.5% for 1.37 mg/cm(2).
Soiling; Glass cover; Spin-coating technique; SEM images; PXRD; External quantum efficiency; Current-voltage measurements; Solar spectral irradiance