The effects of substrate bias on phase stability and properties of sputter-deposited tungsten carbide |
| Autores |
Krzanowski J.E. , ENDRINO ARMENTEROS, JOSÉ LUIS |
| Publicación externa |
Si |
| Medio |
MATERIALS LETTERS |
| Alcance |
Article |
| Naturaleza |
Científica |
| Cuartil JCR |
2 |
| Cuartil SJR |
1 |
| Impacto JCR |
1.186 |
| Impacto SJR |
0.652 |
| Web |
https://www.scopus.com/inward/record.uri?eid=2-s2.0-4944222391&doi=10.1016%2fj.matlet.2004.04.036&partnerID=40&md5=d8bafc162cff8313652e2ef0d01fe2e0 |
| Fecha de publicacion |
01/01/2004 |
| ISI |
000224449500014 |
| Scopus Id |
2-s2.0-4944222391 |
| DOI |
10.1016/j.matlet.2004.04.036 |
| Abstract |
The effects of substrate bias on phase formation and physical properties of rf magnetron sputter-deposited tungsten carbide films have been investigated in this work. Films were deposited at 275°C using bias levels ranging from 0 to -150 V and at room temperature and -160 V. At low bias levels, the films were primarily composed of the WC1-x/W2(C,O) phases, both of which have the B1 structure, and the fraction of the hexagonal W2C phase increased with bias level. The increased substrate bias levels also correlated with a reduction in oxygen content, suggesting that reducing oxygen content promotes formation of the W2C phase. However, the film deposited at room temperature and -160 V bias had an oxygen content of only 3%, yet did not form the W2C phase, indicating a minimum level of thermal activation is also required to form W2C. Increasing the bias voltage also resulting in increases in film hardness, modulus and compressive residual stress, while reducing resistivity. © 2004 Elsevier B.V. All rights reserved. |
| Palabras clave |
Composition; Compressive stress; Elastic moduli; Electric potential; Hardness; Magnetrons; Residual stresses; Sputter deposition; Thermal effects; Tungsten carbide; Atomic ratio; Phase formation; Phase stability; Sublattice; Thin films |