| Title |
Efficient SrO-based thermochemical energy storage using a closed-loop pressure swing |
| Authors |
Amghar, Nabil , Sanchez-Jimenez, Pedro E. , ORTIZ DOMÍNGUEZ, CARLOS, Perez-Maqueda, Luis A. , Perejon, Antonio |
| External publication |
No |
| Means |
Appl Therm Eng |
| Scope |
Article |
| Nature |
Científica |
| JCR Quartile |
1 |
| SJR Quartile |
1 |
| Publication date |
25/11/2023 |
| ISI |
001067847700001 |
| DOI |
10.1016/j.applthermaleng.2023.121411 |
| Abstract |
The SrCO3/SrO system has recently attracted interest for thermochemical energy storage due to the high energy densities potentially attainable. However, the high temperatures needed to promote calcination involve a sintering-induced deactivation of SrO to carbonation. In this work, SrO-based samples have been tested using a closed-loop pressure swing approach involving calcinations and carbonations at absolute pressures of 0.01 bar and 1 bar CO2, respectively. Using low CO2 absolute pressure for calcination decreases the reaction temperature to 900 degrees C, thus reducing the deactivation of SrO. Moreover, the use of additives further improves the reactivity of the samples. The addition of ZrO2 and MgO by mechanical mixing and acetic acid treatment, respectively, results in samples with very high multicycle performance, yielding material energy storage densities after twenty cycles above 5.0 GJ/m3. These results significantly improve those obtained for similar samples in which calcinations and carbonations were carried out at an absolute pressure of 1 bar CO2. Regarding the integration of the thermochemical energy storage into concentrating solar power plants, calcining SrO-based materials at low pressure increases the net thermal-to-electric efficiencies by up to 6 % points compared to CaO-based materials calcined at the same conditions. The importance of experimental conditions and precursors in the multicycle behaviour of SrO-based materials for thermochemical energy storage is emphasized. |
| Keywords |
Thermochemical energy storage; Low absolute CO 2 pressure; SrCO3; Strontium-looping; Concentrated solar power; Closed loop |